S30600 Stainless Steel vs. EN 1.4580 Stainless Steel

Both S30600 stainless steel and EN 1.4580 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.4580 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
40
Fatigue Strength, MPa 250
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 430
430
Tensile Strength: Ultimate (UTS), MPa 610
620
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 350
290
Maximum Temperature: Corrosion, °C 410
480
Maximum Temperature: Mechanical, °C 950
950
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
22
Density, g/cm3 7.6
7.9
Embodied Carbon, kg CO2/kg material 3.6
4.3
Embodied Energy, MJ/kg 51
60
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 18
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
200
Resilience: Unit (Modulus of Resilience), kJ/m3 190
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0 to 0.018
0 to 0.080
Chromium (Cr), % 17 to 18.5
16.5 to 18.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
61.4 to 71
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
2.0 to 2.5
Nickel (Ni), % 14 to 15.5
10.5 to 13.5
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 3.7 to 4.3
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015