S30600 Stainless Steel vs. EN 1.4911 Stainless Steel

Both S30600 stainless steel and EN 1.4911 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.4911 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 45
11
Fatigue Strength, MPa 250
530
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 430
640
Tensile Strength: Ultimate (UTS), MPa 610
1070
Tensile Strength: Yield (Proof), MPa 270
970

Thermal Properties

Latent Heat of Fusion, J/g 350
270
Maximum Temperature: Corrosion, °C 410
430
Maximum Temperature: Mechanical, °C 950
700
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1330
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
20
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
20
Density, g/cm3 7.6
7.9
Embodied Carbon, kg CO2/kg material 3.6
3.4
Embodied Energy, MJ/kg 51
49
Embodied Water, L/kg 150
130

Common Calculations

PREN (Pitting Resistance) 18
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
120
Resilience: Unit (Modulus of Resilience), kJ/m3 190
2410
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
38
Strength to Weight: Bending, points 21
30
Thermal Diffusivity, mm2/s 3.7
5.4
Thermal Shock Resistance, points 14
37

Alloy Composition

Boron (B), % 0
0.0050 to 0.015
Carbon (C), % 0 to 0.018
0.050 to 0.12
Chromium (Cr), % 17 to 18.5
9.8 to 11.2
Cobalt (Co), % 0
5.0 to 7.0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
75.7 to 83.8
Manganese (Mn), % 0 to 2.0
0.3 to 1.3
Molybdenum (Mo), % 0 to 0.2
0.5 to 1.0
Nickel (Ni), % 14 to 15.5
0.2 to 1.2
Niobium (Nb), % 0
0.2 to 0.5
Nitrogen (N), % 0
0 to 0.035
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 3.7 to 4.3
0.1 to 0.8
Sulfur (S), % 0 to 0.020
0 to 0.015
Tungsten (W), % 0
0 to 0.7
Vanadium (V), % 0
0.1 to 0.4