S30600 Stainless Steel vs. EN 1.5535 Steel

Both S30600 stainless steel and EN 1.5535 steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.5535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 45
11 to 22
Fatigue Strength, MPa 250
210 to 320
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
62 to 72
Shear Modulus, GPa 76
73
Shear Strength, MPa 430
320 to 370
Tensile Strength: Ultimate (UTS), MPa 610
450 to 1490
Tensile Strength: Yield (Proof), MPa 270
300 to 500

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 950
400
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.9
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.4
Embodied Energy, MJ/kg 51
19
Embodied Water, L/kg 150
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 190
240 to 680
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
16 to 53
Strength to Weight: Bending, points 21
17 to 37
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 14
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.018
0.2 to 0.25
Chromium (Cr), % 17 to 18.5
0 to 0.3
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 58.9 to 65.3
97.6 to 98.9
Manganese (Mn), % 0 to 2.0
0.9 to 1.2
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 15.5
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 3.7 to 4.3
0 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.025