S30600 Stainless Steel vs. EN 1.7361 Steel

Both S30600 stainless steel and EN 1.7361 steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is EN 1.7361 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
300
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 45
11
Fatigue Strength, MPa 250
480
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Shear Strength, MPa 430
600
Tensile Strength: Ultimate (UTS), MPa 610
1010
Tensile Strength: Yield (Proof), MPa 270
780

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 950
470
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 19
3.6
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.7
Embodied Energy, MJ/kg 51
22
Embodied Water, L/kg 150
60

Common Calculations

PREN (Pitting Resistance) 18
4.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110
Resilience: Unit (Modulus of Resilience), kJ/m3 190
1590
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
36
Strength to Weight: Bending, points 21
29
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 14
29

Alloy Composition

Carbon (C), % 0 to 0.018
0.28 to 0.35
Chromium (Cr), % 17 to 18.5
2.8 to 3.3
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.9 to 65.3
94.1 to 96.2
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.2
0.3 to 0.5
Nickel (Ni), % 14 to 15.5
0 to 0.6
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 3.7 to 4.3
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.035