S30600 Stainless Steel vs. SAE-AISI T1 Steel

Both S30600 stainless steel and SAE-AISI T1 steel are iron alloys. They have 67% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S30600 stainless steel and the bottom bar is SAE-AISI T1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 610
770 to 2130

Thermal Properties

Latent Heat of Fusion, J/g 350
240
Melting Completion (Liquidus), °C 1380
1810
Melting Onset (Solidus), °C 1330
1750
Specific Heat Capacity, J/kg-K 490
410
Thermal Conductivity, W/m-K 14
20
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 19
45
Density, g/cm3 7.6
9.3
Embodied Carbon, kg CO2/kg material 3.6
8.2
Embodied Energy, MJ/kg 51
130
Embodied Water, L/kg 150
90

Common Calculations

PREN (Pitting Resistance) 18
34
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 22
23 to 64
Strength to Weight: Bending, points 21
20 to 40
Thermal Diffusivity, mm2/s 3.7
5.2
Thermal Shock Resistance, points 14
23 to 64

Alloy Composition

Carbon (C), % 0 to 0.018
0.65 to 0.8
Chromium (Cr), % 17 to 18.5
3.8 to 4.5
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 58.9 to 65.3
73.2 to 77.2
Manganese (Mn), % 0 to 2.0
0.1 to 0.4
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 15.5
0 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 3.7 to 4.3
0.2 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.030
Tungsten (W), % 0
17.3 to 18.8
Vanadium (V), % 0
0.9 to 1.3