S30601 Stainless Steel vs. Austempered Cast Iron
Both S30601 stainless steel and austempered cast iron are iron alloys. They have 63% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is S30601 stainless steel and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 270 to 490 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 |
| Elongation at Break, % | 37 | |
| 1.1 to 13 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 62 to 69 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 860 to 1800 |
| Tensile Strength: Yield (Proof), MPa | 300 | |
| 560 to 1460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 280 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1380 |
| Melting Onset (Solidus), °C | 1310 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 490 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 20 | |
| 2.9 |
| Density, g/cm3 | 7.6 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 55 | |
| 25 |
| Embodied Water, L/kg | 150 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 19 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 880 to 3970 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 32 to 66 |
| Strength to Weight: Bending, points | 22 | |
| 27 to 44 |
| Thermal Shock Resistance, points | 16 | |
| 25 to 53 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Arsenic (As), % | 0 | |
| 0 to 0.020 |
| Carbon (C), % | 0 to 0.015 | |
| 3.4 to 3.8 |
| Chromium (Cr), % | 17 to 18 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 to 0.8 |
| Iron (Fe), % | 56.9 to 60.5 | |
| 89.6 to 94 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.040 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.3 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.2 | |
| 0 to 0.3 |
| Nickel (Ni), % | 17 to 18 | |
| 0 to 2.0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 5.0 to 5.6 | |
| 2.3 to 2.7 |
| Sulfur (S), % | 0 to 0.013 | |
| 0 to 0.020 |
| Tin (Sn), % | 0 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |