S30601 Stainless Steel vs. Z21210 Zinc

S30601 stainless steel belongs to the iron alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 8 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.

For each property being compared, the top bar is S30601 stainless steel and the bottom bar is Z21210 zinc.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.6
7.1
Melting Completion (Liquidus), °C 1360
420
Melting Onset (Solidus), °C 1310
420
Specific Heat Capacity, J/kg-K 500
400
Strength to Weight: Axial, points 24
5.7 to 6.4
Strength to Weight: Bending, points 22
8.6 to 9.4
Tensile Strength: Ultimate (UTS), MPa 660
150 to 170
Thermal Expansion, µm/m-K 15
32