S30615 Stainless Steel vs. AWS E310

Both S30615 stainless steel and AWS E310 are iron alloys. They have 84% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is S30615 stainless steel and the bottom bar is AWS E310.

UNS S30615 Stainless Steel AWS E310 (W31010) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		39
Elongation at Break, %		34

Poisson's Ratio		0.28
Poisson's Ratio		0.27

Shear Modulus, GPa		75
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		690
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		340
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1370
Melting Completion (Liquidus), °C		1400

Melting Onset (Solidus), °C		1320
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		480

Thermal Conductivity, W/m-K		14
Thermal Conductivity, W/m-K		14

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		19
Base Metal Price, % relative		26

Density, g/cm³		7.6
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		3.7
Embodied Carbon, kg CO₂/kg material		4.6

Embodied Energy, MJ/kg		53
Embodied Energy, MJ/kg		65

Embodied Water, L/kg		170
Embodied Water, L/kg		200

Common Calculations

PREN (Pitting Resistance)		18
PREN (Pitting Resistance)		28

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		25
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		23
Strength to Weight: Bending, points		20

Thermal Diffusivity, mm²/s		3.7
Thermal Diffusivity, mm²/s		3.7

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		15

Alloy Composition

Aluminum (Al), %		0.8 to 1.5
Aluminum (Al), %		0

Carbon (C), %		0.16 to 0.24
Carbon (C), %		0.080 to 0.2

Chromium (Cr), %		17 to 19.5
Chromium (Cr), %		25 to 28

Copper (Cu), %		0
Copper (Cu), %		0 to 0.75

Iron (Fe), %		56.7 to 65.3
Iron (Fe), %		44.5 to 53.9

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		1.0 to 2.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.75

Nickel (Ni), %		13.5 to 16
Nickel (Ni), %		20 to 22.5

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		3.2 to 4.0
Silicon (Si), %		0 to 0.75

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030