S30615 Stainless Steel vs. AWS E410

Both S30615 stainless steel and AWS E410 are iron alloys. They have 75% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S30615 stainless steel and the bottom bar is AWS E410.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		39
Elongation at Break, %		23

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		75
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		690
Tensile Strength: Ultimate (UTS), MPa		580

Tensile Strength: Yield (Proof), MPa		310
Tensile Strength: Yield (Proof), MPa		440

Thermal Properties

Latent Heat of Fusion, J/g		340
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		1370
Melting Completion (Liquidus), °C		1450

Melting Onset (Solidus), °C		1320
Melting Onset (Solidus), °C		1400

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		480

Thermal Conductivity, W/m-K		14
Thermal Conductivity, W/m-K		28

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		19
Base Metal Price, % relative		7.5

Density, g/cm³		7.6
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		3.7
Embodied Carbon, kg CO₂/kg material		2.0

Embodied Energy, MJ/kg		53
Embodied Energy, MJ/kg		28

Embodied Water, L/kg		170
Embodied Water, L/kg		100

Common Calculations

PREN (Pitting Resistance)		18
PREN (Pitting Resistance)		13

Resilience: Ultimate (Unit Rupture Work), MJ/m³		220
Resilience: Ultimate (Unit Rupture Work), MJ/m³		120

Resilience: Unit (Modulus of Resilience), kJ/m³		260
Resilience: Unit (Modulus of Resilience), kJ/m³		500

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		25
Strength to Weight: Axial, points		21

Strength to Weight: Bending, points		23
Strength to Weight: Bending, points		20

Thermal Diffusivity, mm²/s		3.7
Thermal Diffusivity, mm²/s		7.5

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		16

Alloy Composition

Aluminum (Al), %		0.8 to 1.5
Aluminum (Al), %		0

Carbon (C), %		0.16 to 0.24
Carbon (C), %		0 to 0.12

Chromium (Cr), %		17 to 19.5
Chromium (Cr), %		11 to 13.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.75

Iron (Fe), %		56.7 to 65.3
Iron (Fe), %		82.2 to 89

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.75

Nickel (Ni), %		13.5 to 16
Nickel (Ni), %		0 to 0.7

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		3.2 to 4.0
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030