S30615 Stainless Steel vs. C95410 Bronze
S30615 stainless steel belongs to the iron alloys classification, while C95410 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S30615 stainless steel and the bottom bar is C95410 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 160 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 39 | |
| 9.1 to 13 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 620 to 740 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 260 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 230 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1040 |
| Melting Onset (Solidus), °C | 1320 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 440 |
| Thermal Conductivity, W/m-K | 14 | |
| 59 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 28 |
| Density, g/cm3 | 7.6 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 53 | |
| 54 |
| Embodied Water, L/kg | 170 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 | |
| 57 to 64 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 280 to 630 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 25 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 23 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 16 |
| Thermal Shock Resistance, points | 16 | |
| 22 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.8 to 1.5 | |
| 10 to 11.5 |
| Carbon (C), % | 0.16 to 0.24 | |
| 0 |
| Chromium (Cr), % | 17 to 19.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 83 to 85.5 |
| Iron (Fe), % | 56.7 to 65.3 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 13.5 to 16 | |
| 1.5 to 2.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 3.2 to 4.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |