S31060 Stainless Steel vs. SAE-AISI 52100 Steel

Both S31060 stainless steel and SAE-AISI 52100 steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S31060 stainless steel and the bottom bar is SAE-AISI 52100 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
10 to 20
Fatigue Strength, MPa 290
250 to 340
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
72
Shear Strength, MPa 480
370 to 420
Tensile Strength: Ultimate (UTS), MPa 680
590 to 2010
Tensile Strength: Yield (Proof), MPa 310
360 to 560

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1080
430
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 16
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.5
Embodied Energy, MJ/kg 48
20
Embodied Water, L/kg 170
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
54 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 250
350 to 840
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
21 to 72
Strength to Weight: Bending, points 22
20 to 45
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 15
19 to 61

Alloy Composition

Boron (B), % 0.0010 to 0.010
0
Carbon (C), % 0.050 to 0.1
0.93 to 1.1
Cerium (Ce), % 0 to 0.070
0
Chromium (Cr), % 22 to 24
1.4 to 1.6
Iron (Fe), % 61.4 to 67.8
96.5 to 97.3
Lanthanum (La), % 0 to 0.070
0
Manganese (Mn), % 0 to 1.0
0.25 to 0.45
Nickel (Ni), % 10 to 12.5
0
Nitrogen (N), % 0.18 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015