S31727 Stainless Steel vs. EN 1.1181 Steel

Both S31727 stainless steel and EN 1.1181 steel are iron alloys. They have 59% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S31727 stainless steel and the bottom bar is EN 1.1181 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
19 to 20
Fatigue Strength, MPa 240
190 to 260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 430
350 to 390
Tensile Strength: Ultimate (UTS), MPa 630
560 to 620
Tensile Strength: Yield (Proof), MPa 270
280 to 380

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 16
11

Otherwise Unclassified Properties

Base Metal Price, % relative 24
2.1
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 4.7
1.4
Embodied Energy, MJ/kg 64
19
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 190
210 to 380
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
20 to 22
Strength to Weight: Bending, points 20
19 to 21
Thermal Shock Resistance, points 14
19 to 21

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.39
Chromium (Cr), % 17.5 to 19
0 to 0.4
Copper (Cu), % 2.8 to 4.0
0
Iron (Fe), % 53.7 to 61.3
97.4 to 99.18
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 3.8 to 4.5
0 to 0.1
Nickel (Ni), % 14.5 to 16.5
0 to 0.4
Nitrogen (N), % 0.15 to 0.21
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035