S31730 Stainless Steel vs. N07041 Nickel
S31730 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is S31730 stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 40 | |
| 14 |
| Fatigue Strength, MPa | 170 | |
| 540 |
| Shear Strength, MPa | 370 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1390 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 99 | |
| 2510 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 19 | |
| 47 |
| Strength to Weight: Bending, points | 18 | |
| 34 |
| Thermal Shock Resistance, points | 12 | |
| 38 |