S32615 Stainless Steel vs. AISI W5 Steel

Both S32615 stainless steel and AISI W5 steel are iron alloys. They have 53% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is S32615 stainless steel and the bottom bar is AISI W5 steel.

UNS S32615 Stainless Steel AISI W5 (T72305) Water-Hardening Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		75
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		600 to 2360

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1350
Melting Completion (Liquidus), °C		1450

Melting Onset (Solidus), °C		1310
Melting Onset (Solidus), °C		1410

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		24
Base Metal Price, % relative		2.3

Density, g/cm³		7.6
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		4.4
Embodied Carbon, kg CO₂/kg material		1.6

Embodied Energy, MJ/kg		63
Embodied Energy, MJ/kg		21

Embodied Water, L/kg		170
Embodied Water, L/kg		48

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		23
Strength to Weight: Axial, points		21 to 84

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		20 to 50

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		20 to 78

Alloy Composition

Carbon (C), %		0 to 0.070
Carbon (C), %		1.1 to 1.2

Chromium (Cr), %		16.5 to 19.5
Chromium (Cr), %		0.4 to 0.6

Copper (Cu), %		1.5 to 2.5
Copper (Cu), %		0 to 0.2

Iron (Fe), %		46.4 to 57.9
Iron (Fe), %		96.6 to 98.4

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		0.1 to 0.4

Molybdenum (Mo), %		0.3 to 1.5
Molybdenum (Mo), %		0 to 0.1

Nickel (Ni), %		19 to 22
Nickel (Ni), %		0 to 0.2

Phosphorus (P), %		0 to 0.045
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		4.8 to 6.0
Silicon (Si), %		0.1 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0
Tungsten (W), %		0 to 0.15

Vanadium (V), %		0
Vanadium (V), %		0 to 0.1