S32615 Stainless Steel vs. SAE-AISI M43 Steel
Both S32615 stainless steel and SAE-AISI M43 steel are iron alloys. They have 58% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is S32615 stainless steel and the bottom bar is SAE-AISI M43 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 810 to 2290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 270 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1550 |
| Melting Onset (Solidus), °C | 1310 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 450 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 33 |
| Density, g/cm3 | 7.6 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 8.5 |
| Embodied Energy, MJ/kg | 63 | |
| 120 |
| Embodied Water, L/kg | 170 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 35 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 23 | |
| 27 to 77 |
| Strength to Weight: Bending, points | 21 | |
| 24 to 47 |
| Thermal Shock Resistance, points | 15 | |
| 25 to 71 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 1.2 to 1.3 |
| Chromium (Cr), % | 16.5 to 19.5 | |
| 3.5 to 4.3 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 46.4 to 57.9 | |
| 70.8 to 76 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0.3 to 1.5 | |
| 7.5 to 8.5 |
| Nickel (Ni), % | 19 to 22 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.030 |
| Silicon (Si), % | 4.8 to 6.0 | |
| 0.15 to 0.65 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 2.3 to 3.0 |
| Vanadium (V), % | 0 | |
| 1.5 to 1.8 |