S32750 Stainless Steel vs. EN 1.7336 Steel

Both S32750 stainless steel and EN 1.7336 steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32750 stainless steel and the bottom bar is EN 1.7336 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 17
22
Fatigue Strength, MPa 360
240 to 310
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 530
370
Tensile Strength: Ultimate (UTS), MPa 860
590
Tensile Strength: Yield (Proof), MPa 590
340 to 440

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 21
3.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.1
1.6
Embodied Energy, MJ/kg 56
21
Embodied Water, L/kg 180
53

Common Calculations

PREN (Pitting Resistance) 43
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 860
310 to 510
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31
21
Strength to Weight: Bending, points 26
20
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 25
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.17
Chromium (Cr), % 24 to 26
1.0 to 1.5
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 58.1 to 66.8
95.6 to 97.7
Manganese (Mn), % 0 to 1.2
0.4 to 0.65
Molybdenum (Mo), % 3.0 to 5.0
0.45 to 0.65
Nickel (Ni), % 6.0 to 8.0
0 to 0.3
Nitrogen (N), % 0.24 to 0.32
0 to 0.012
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0 to 0.8
0.5 to 0.8
Sulfur (S), % 0 to 0.020
0 to 0.0050