S32906 Stainless Steel vs. 2117 Aluminum

S32906 stainless steel belongs to the iron alloys classification, while 2117 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S32906 stainless steel and the bottom bar is 2117 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
70
Elastic (Young's, Tensile) Modulus, GPa 210
71
Elongation at Break, % 28
26
Fatigue Strength, MPa 460
95
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 81
27
Shear Strength, MPa 550
200
Tensile Strength: Ultimate (UTS), MPa 850
300
Tensile Strength: Yield (Proof), MPa 620
170

Thermal Properties

Latent Heat of Fusion, J/g 300
400
Maximum Temperature: Mechanical, °C 1100
220
Melting Completion (Liquidus), °C 1430
650
Melting Onset (Solidus), °C 1380
550
Specific Heat Capacity, J/kg-K 480
880
Thermal Conductivity, W/m-K 13
150
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
40
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
120

Otherwise Unclassified Properties

Base Metal Price, % relative 20
10
Density, g/cm3 7.7
3.0
Embodied Carbon, kg CO2/kg material 3.7
8.2
Embodied Energy, MJ/kg 52
150
Embodied Water, L/kg 190
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
64
Resilience: Unit (Modulus of Resilience), kJ/m3 950
190
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
47
Strength to Weight: Axial, points 30
28
Strength to Weight: Bending, points 26
33
Thermal Diffusivity, mm2/s 3.6
59
Thermal Shock Resistance, points 23
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
91 to 97.6
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 28 to 30
0 to 0.1
Copper (Cu), % 0 to 0.8
2.2 to 4.5
Iron (Fe), % 56.6 to 63.6
0 to 0.7
Magnesium (Mg), % 0
0.2 to 1.0
Manganese (Mn), % 0.8 to 1.5
0.4 to 1.0
Molybdenum (Mo), % 1.5 to 2.6
0
Nickel (Ni), % 5.8 to 7.5
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0.2 to 0.8
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.25
Zirconium (Zr), % 0
0 to 0.25
Residuals, % 0
0 to 0.15