S32906 Stainless Steel vs. 336.0 Aluminum

S32906 stainless steel belongs to the iron alloys classification, while 336.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S32906 stainless steel and the bottom bar is 336.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
110 to 130
Elastic (Young's, Tensile) Modulus, GPa 210
75
Elongation at Break, % 28
0.5
Fatigue Strength, MPa 460
80 to 93
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 81
28
Shear Strength, MPa 550
190 to 250
Tensile Strength: Ultimate (UTS), MPa 850
250 to 320
Tensile Strength: Yield (Proof), MPa 620
190 to 300

Thermal Properties

Latent Heat of Fusion, J/g 300
570
Maximum Temperature: Mechanical, °C 1100
210
Melting Completion (Liquidus), °C 1430
570
Melting Onset (Solidus), °C 1380
540
Specific Heat Capacity, J/kg-K 480
890
Thermal Conductivity, W/m-K 13
120
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
29
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
95

Otherwise Unclassified Properties

Base Metal Price, % relative 20
11
Density, g/cm3 7.7
2.8
Embodied Carbon, kg CO2/kg material 3.7
7.9
Embodied Energy, MJ/kg 52
140
Embodied Water, L/kg 190
1010

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
1.1 to 1.6
Resilience: Unit (Modulus of Resilience), kJ/m3 950
250 to 580
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 25
51
Strength to Weight: Axial, points 30
25 to 32
Strength to Weight: Bending, points 26
32 to 38
Thermal Diffusivity, mm2/s 3.6
48
Thermal Shock Resistance, points 23
12 to 16

Alloy Composition

Aluminum (Al), % 0
79.1 to 85.8
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.8
0.5 to 1.5
Iron (Fe), % 56.6 to 63.6
0 to 1.2
Magnesium (Mg), % 0
0.7 to 1.3
Manganese (Mn), % 0.8 to 1.5
0 to 0.35
Molybdenum (Mo), % 1.5 to 2.6
0
Nickel (Ni), % 5.8 to 7.5
2.0 to 3.0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
11 to 13
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.35