S32906 Stainless Steel vs. 7108 Aluminum

S32906 stainless steel belongs to the iron alloys classification, while 7108 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S32906 stainless steel and the bottom bar is 7108 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
69
Elongation at Break, % 28
11
Fatigue Strength, MPa 460
120
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 81
26
Shear Strength, MPa 550
210
Tensile Strength: Ultimate (UTS), MPa 850
350
Tensile Strength: Yield (Proof), MPa 620
290

Thermal Properties

Latent Heat of Fusion, J/g 300
380
Maximum Temperature: Mechanical, °C 1100
210
Melting Completion (Liquidus), °C 1430
630
Melting Onset (Solidus), °C 1380
530
Specific Heat Capacity, J/kg-K 480
880
Thermal Conductivity, W/m-K 13
150
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
39
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
120

Otherwise Unclassified Properties

Base Metal Price, % relative 20
9.5
Density, g/cm3 7.7
2.9
Embodied Carbon, kg CO2/kg material 3.7
8.3
Embodied Energy, MJ/kg 52
150
Embodied Water, L/kg 190
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
38
Resilience: Unit (Modulus of Resilience), kJ/m3 950
620
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
47
Strength to Weight: Axial, points 30
34
Strength to Weight: Bending, points 26
38
Thermal Diffusivity, mm2/s 3.6
59
Thermal Shock Resistance, points 23
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
92.4 to 94.7
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.8
0 to 0.050
Iron (Fe), % 56.6 to 63.6
0 to 0.1
Magnesium (Mg), % 0
0.7 to 1.4
Manganese (Mn), % 0.8 to 1.5
0 to 0.050
Molybdenum (Mo), % 1.5 to 2.6
0
Nickel (Ni), % 5.8 to 7.5
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 0
4.5 to 5.5
Zirconium (Zr), % 0
0.12 to 0.25
Residuals, % 0
0 to 0.15