S32906 Stainless Steel vs. Z13004 Zinc

S32906 stainless steel belongs to the iron alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S32906 stainless steel and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
87
Elongation at Break, % 28
30
Poisson's Ratio 0.27
0.25
Shear Modulus, GPa 81
35
Tensile Strength: Ultimate (UTS), MPa 850
93
Tensile Strength: Yield (Proof), MPa 620
76

Thermal Properties

Latent Heat of Fusion, J/g 300
110
Maximum Temperature: Mechanical, °C 1100
90
Melting Completion (Liquidus), °C 1430
410
Melting Onset (Solidus), °C 1380
390
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 13
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
37

Otherwise Unclassified Properties

Base Metal Price, % relative 20
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 3.7
2.8
Embodied Energy, MJ/kg 52
53
Embodied Water, L/kg 190
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
26
Resilience: Unit (Modulus of Resilience), kJ/m3 950
33
Stiffness to Weight: Axial, points 15
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 30
3.9
Strength to Weight: Bending, points 26
7.0
Thermal Diffusivity, mm2/s 3.6
44
Thermal Shock Resistance, points 23
2.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0030
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.8
0 to 0.0030
Iron (Fe), % 56.6 to 63.6
0 to 0.0030
Lead (Pb), % 0
0 to 0.0030
Manganese (Mn), % 0.8 to 1.5
0
Molybdenum (Mo), % 1.5 to 2.6
0
Nickel (Ni), % 5.8 to 7.5
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.0010
Zinc (Zn), % 0
99.985 to 100