S33550 Stainless Steel vs. AISI 347H Stainless Steel
Both S33550 stainless steel and AISI 347H stainless steel are iron alloys. Both are furnished in the annealed condition. They have 84% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is S33550 stainless steel and the bottom bar is AISI 347H stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 40 | |
| 39 |
| Fatigue Strength, MPa | 270 | |
| 200 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Rockwell B Hardness | 82 | |
| 81 |
| Shear Modulus, GPa | 79 | |
| 77 |
| Shear Strength, MPa | 470 | |
| 400 |
| Tensile Strength: Ultimate (UTS), MPa | 680 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 470 | |
| 480 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 940 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1430 |
| Melting Onset (Solidus), °C | 1360 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 16 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 19 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 3.6 |
| Embodied Energy, MJ/kg | 61 | |
| 52 |
| Embodied Water, L/kg | 190 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 30 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 21 |
| Strength to Weight: Bending, points | 22 | |
| 20 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 4.2 |
| Thermal Shock Resistance, points | 15 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.1 | |
| 0.040 to 0.1 |
| Cerium (Ce), % | 0.025 to 0.070 | |
| 0 |
| Chromium (Cr), % | 25 to 28 | |
| 17 to 19 |
| Iron (Fe), % | 48.8 to 58.2 | |
| 64.1 to 74 |
| Lanthanum (La), % | 0.025 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 2.0 |
| Nickel (Ni), % | 16.5 to 20 | |
| 9.0 to 13 |
| Niobium (Nb), % | 0.050 to 0.15 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0.18 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |