S33550 Stainless Steel vs. EN 1.4107 Stainless Steel

Both S33550 stainless steel and EN 1.4107 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S33550 stainless steel and the bottom bar is EN 1.4107 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
18 to 21
Fatigue Strength, MPa 270
260 to 350
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 680
620 to 700
Tensile Strength: Yield (Proof), MPa 310
400 to 570

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 470
390
Maximum Temperature: Mechanical, °C 1100
740
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
27
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 24
7.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
2.1
Embodied Energy, MJ/kg 61
30
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 30
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 250
420 to 840
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
22 to 25
Strength to Weight: Bending, points 22
21 to 22
Thermal Diffusivity, mm2/s 3.9
7.2
Thermal Shock Resistance, points 15
22 to 25

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.1
Cerium (Ce), % 0.025 to 0.070
0
Chromium (Cr), % 25 to 28
11.5 to 12.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 48.8 to 58.2
83.8 to 87.2
Lanthanum (La), % 0.025 to 0.070
0
Manganese (Mn), % 0 to 1.5
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 16.5 to 20
0.8 to 1.5
Niobium (Nb), % 0.050 to 0.15
0
Nitrogen (N), % 0.18 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0
0 to 0.080