S33550 Stainless Steel vs. EN 1.4662 Stainless Steel

Both S33550 stainless steel and EN 1.4662 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S33550 stainless steel and the bottom bar is EN 1.4662 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
28
Fatigue Strength, MPa 270
430 to 450
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 79
79
Shear Strength, MPa 470
520 to 540
Tensile Strength: Ultimate (UTS), MPa 680
810 to 830
Tensile Strength: Yield (Proof), MPa 310
580 to 620

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 470
440
Maximum Temperature: Mechanical, °C 1100
1090
Melting Completion (Liquidus), °C 1400
1430
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 24
16
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.2
Embodied Energy, MJ/kg 61
45
Embodied Water, L/kg 190
170

Common Calculations

PREN (Pitting Resistance) 30
33
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
210
Resilience: Unit (Modulus of Resilience), kJ/m3 250
840 to 940
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
29 to 30
Strength to Weight: Bending, points 22
25
Thermal Diffusivity, mm2/s 3.9
3.9
Thermal Shock Resistance, points 15
22

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.030
Cerium (Ce), % 0.025 to 0.070
0
Chromium (Cr), % 25 to 28
23 to 25
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 48.8 to 58.2
62.6 to 70.2
Lanthanum (La), % 0.025 to 0.070
0
Manganese (Mn), % 0 to 1.5
2.5 to 4.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 16.5 to 20
3.0 to 4.5
Niobium (Nb), % 0.050 to 0.15
0
Nitrogen (N), % 0.18 to 0.25
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.0050