S40930 Stainless Steel vs. AWS BVAg-6b

S40930 stainless steel belongs to the iron alloys classification, while AWS BVAg-6b belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is S40930 stainless steel and the bottom bar is AWS BVAg-6b.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
93
Poisson's Ratio 0.28
0.35
Shear Modulus, GPa 75
35
Tensile Strength: Ultimate (UTS), MPa 430
180

Thermal Properties

Latent Heat of Fusion, J/g 270
160
Melting Completion (Liquidus), °C 1450
870
Melting Onset (Solidus), °C 1410
780
Specific Heat Capacity, J/kg-K 480
310
Thermal Expansion, µm/m-K 10
19

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.7
Embodied Carbon, kg CO2/kg material 2.3
49
Embodied Energy, MJ/kg 32
770

Common Calculations

Stiffness to Weight: Axial, points 14
5.3
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 16
5.1
Strength to Weight: Bending, points 16
7.3
Thermal Shock Resistance, points 16
7.4

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.030
0 to 0.0050
Chromium (Cr), % 10.5 to 11.7
0
Copper (Cu), % 0
49 to 51
Iron (Fe), % 84.7 to 89.4
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.080 to 0.75
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.0020
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0.050 to 0.2
0
Zinc (Zn), % 0
0 to 0.0010