S40930 Stainless Steel vs. SAE-AISI 1070 Steel

Both S40930 stainless steel and SAE-AISI 1070 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S40930 stainless steel and the bottom bar is SAE-AISI 1070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
10 to 13
Fatigue Strength, MPa 130
270 to 350
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
72
Shear Strength, MPa 270
380 to 460
Tensile Strength: Ultimate (UTS), MPa 430
640 to 760
Tensile Strength: Yield (Proof), MPa 190
420 to 560

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 710
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
50
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
10
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
12

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 32
19
Embodied Water, L/kg 94
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
59 to 86
Resilience: Unit (Modulus of Resilience), kJ/m3 94
470 to 850
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 16
23 to 27
Strength to Weight: Bending, points 16
21 to 24
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 16
21 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0.65 to 0.75
Chromium (Cr), % 10.5 to 11.7
0
Iron (Fe), % 84.7 to 89.4
98.3 to 98.8
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.080 to 0.75
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.020
0 to 0.050
Titanium (Ti), % 0.050 to 0.2
0