MakeItFrom.com
Menu (ESC)

S40977 Stainless Steel vs. AWS BAg-23

S40977 stainless steel belongs to the iron alloys classification, while AWS BAg-23 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is AWS BAg-23.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
90
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 76
33
Tensile Strength: Ultimate (UTS), MPa 510
170

Thermal Properties

Latent Heat of Fusion, J/g 270
130
Melting Completion (Liquidus), °C 1440
970
Melting Onset (Solidus), °C 1400
960
Specific Heat Capacity, J/kg-K 480
270
Thermal Expansion, µm/m-K 10
20

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 14
5.0
Stiffness to Weight: Bending, points 25
15
Strength to Weight: Axial, points 18
4.7
Strength to Weight: Bending, points 18
6.8
Thermal Shock Resistance, points 18
6.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 83.9 to 89.2
0
Manganese (Mn), % 0 to 1.5
13.9 to 16
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
84 to 86
Sulfur (S), % 0 to 0.015
0
Residuals, % 0
0 to 0.15