S40977 Stainless Steel vs. EN 1.0215 Steel

Both S40977 stainless steel and EN 1.0215 steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.0215 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
100
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
25
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 320
230
Tensile Strength: Ultimate (UTS), MPa 510
350
Tensile Strength: Yield (Proof), MPa 310
250

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
53
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 97
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
79
Resilience: Unit (Modulus of Resilience), kJ/m3 250
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
13
Strength to Weight: Bending, points 18
14
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 18
11

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.14
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 83.9 to 89.2
98.7 to 100
Manganese (Mn), % 0 to 1.5
0 to 0.7
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.045