S40977 Stainless Steel vs. EN 1.1060 Steel

Both S40977 stainless steel and EN 1.1060 steel are iron alloys. They have 87% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.1060 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 510
490 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 97
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
17 to 61
Strength to Weight: Bending, points 18
18 to 41
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 18
16 to 55

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.39
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.9 to 89.2
98.2 to 99.16
Manganese (Mn), % 0 to 1.5
0.5 to 0.8
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0.020 to 0.035