S40977 Stainless Steel vs. EN 1.4415 Stainless Steel

Both S40977 stainless steel and EN 1.4415 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.4415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
17 to 20
Fatigue Strength, MPa 200
470 to 510
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 320
520 to 570
Tensile Strength: Ultimate (UTS), MPa 510
830 to 930
Tensile Strength: Yield (Proof), MPa 310
730 to 840

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 720
790
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
19
Thermal Expansion, µm/m-K 10
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
13
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.9
3.6
Embodied Energy, MJ/kg 27
51
Embodied Water, L/kg 97
120

Common Calculations

PREN (Pitting Resistance) 12
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
150 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 250
1350 to 1790
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
29 to 33
Strength to Weight: Bending, points 18
25 to 27
Thermal Diffusivity, mm2/s 6.7
5.1
Thermal Shock Resistance, points 18
30 to 34

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 10.5 to 12.5
11.5 to 13.5
Iron (Fe), % 83.9 to 89.2
75.9 to 82.4
Manganese (Mn), % 0 to 1.5
0 to 0.5
Molybdenum (Mo), % 0
1.5 to 2.5
Nickel (Ni), % 0.3 to 1.0
4.5 to 6.5
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.1 to 0.5