S40977 Stainless Steel vs. EN 1.5410 Steel

Both S40977 stainless steel and EN 1.5410 steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.5410 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
20 to 25
Fatigue Strength, MPa 200
290 to 330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 510
560 to 620
Tensile Strength: Yield (Proof), MPa 310
400 to 480

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
51
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.7
Embodied Energy, MJ/kg 27
22
Embodied Water, L/kg 97
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 250
430 to 610
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
20 to 22
Strength to Weight: Bending, points 18
19 to 21
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 18
16 to 18

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.12
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 83.9 to 89.2
96.9 to 98.6
Manganese (Mn), % 0 to 1.5
1.2 to 1.8
Molybdenum (Mo), % 0
0.2 to 0.4
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.020
Vanadium (V), % 0
0.050 to 0.1