S40977 Stainless Steel vs. EN 1.7707 Steel

Both S40977 stainless steel and EN 1.7707 steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.7707 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
300
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
11
Fatigue Strength, MPa 200
500
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 320
600
Tensile Strength: Ultimate (UTS), MPa 510
1010
Tensile Strength: Yield (Proof), MPa 310
800

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
460
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
3.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.9
Embodied Energy, MJ/kg 27
27
Embodied Water, L/kg 97
58

Common Calculations

PREN (Pitting Resistance) 12
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
110
Resilience: Unit (Modulus of Resilience), kJ/m3 250
1690
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
36
Strength to Weight: Bending, points 18
29
Thermal Diffusivity, mm2/s 6.7
11
Thermal Shock Resistance, points 18
29

Alloy Composition

Carbon (C), % 0 to 0.030
0.26 to 0.34
Chromium (Cr), % 10.5 to 12.5
2.3 to 2.7
Iron (Fe), % 83.9 to 89.2
94.7 to 96.8
Manganese (Mn), % 0 to 1.5
0.4 to 0.7
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0.3 to 1.0
0 to 0.6
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.035
Vanadium (V), % 0
0.1 to 0.2