S40977 Stainless Steel vs. EN 1.8153 Steel

Both S40977 stainless steel and EN 1.8153 steel are iron alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is EN 1.8153 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
200 to 570
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 510
670 to 2040

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 720
410
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
45
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
2.1
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
1.8
Embodied Energy, MJ/kg 27
25
Embodied Water, L/kg 97
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
24 to 74
Strength to Weight: Bending, points 18
22 to 46
Thermal Diffusivity, mm2/s 6.7
12
Thermal Shock Resistance, points 18
20 to 62

Alloy Composition

Carbon (C), % 0 to 0.030
0.56 to 0.64
Chromium (Cr), % 10.5 to 12.5
0.2 to 0.4
Iron (Fe), % 83.9 to 89.2
95.7 to 96.9
Manganese (Mn), % 0 to 1.5
0.7 to 1.0
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
1.5 to 2.0
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0
0.1 to 0.2