S40977 Stainless Steel vs. SAE-AISI 1050 Steel

Both S40977 stainless steel and SAE-AISI 1050 steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S40977 stainless steel and the bottom bar is SAE-AISI 1050 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
200 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
11 to 17
Fatigue Strength, MPa 200
260 to 400
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Shear Strength, MPa 320
430 to 470
Tensile Strength: Ultimate (UTS), MPa 510
690 to 790
Tensile Strength: Yield (Proof), MPa 310
390 to 650

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 97
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 250
400 to 1130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
25 to 28
Strength to Weight: Bending, points 18
22 to 24
Thermal Diffusivity, mm2/s 6.7
14
Thermal Shock Resistance, points 18
22 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0.48 to 0.55
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 83.9 to 89.2
98.5 to 98.9
Manganese (Mn), % 0 to 1.5
0.6 to 0.9
Nickel (Ni), % 0.3 to 1.0
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.050