S41003 Stainless Steel vs. EN 1.8961 Steel

Both S41003 stainless steel and EN 1.8961 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S41003 stainless steel and the bottom bar is EN 1.8961 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
19
Fatigue Strength, MPa 200
150
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 320
270
Tensile Strength: Ultimate (UTS), MPa 520
430
Tensile Strength: Yield (Proof), MPa 310
220

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
45
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.7
Embodied Energy, MJ/kg 27
23
Embodied Water, L/kg 97
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
70
Resilience: Unit (Modulus of Resilience), kJ/m3 240
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 7.2
12
Thermal Shock Resistance, points 19
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0 to 0.030
0 to 0.16
Chromium (Cr), % 10.5 to 12.5
0.35 to 0.85
Copper (Cu), % 0
0.2 to 0.6
Iron (Fe), % 83.4 to 89.5
96.1 to 99.3
Manganese (Mn), % 0 to 1.5
0.15 to 0.7
Nickel (Ni), % 0 to 1.5
0 to 0.7
Niobium (Nb), % 0
0 to 0.065
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.035
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14