S41050 Stainless Steel vs. AISI 347H Stainless Steel

Both S41050 stainless steel and AISI 347H stainless steel are iron alloys. Both are furnished in the annealed condition. They have 82% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is AISI 347H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
39
Fatigue Strength, MPa 160
200
Poisson's Ratio 0.28
0.28
Rockwell B Hardness 77
81
Shear Modulus, GPa 76
77
Shear Strength, MPa 300
400
Tensile Strength: Ultimate (UTS), MPa 470
580
Tensile Strength: Yield (Proof), MPa 230
230

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
480
Maximum Temperature: Mechanical, °C 720
940
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
16
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
3.6
Embodied Energy, MJ/kg 27
52
Embodied Water, L/kg 97
150

Common Calculations

PREN (Pitting Resistance) 12
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
180
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 7.2
4.2
Thermal Shock Resistance, points 17
13

Alloy Composition

Carbon (C), % 0 to 0.040
0.040 to 0.1
Chromium (Cr), % 10.5 to 12.5
17 to 19
Iron (Fe), % 84.2 to 88.9
64.1 to 74
Manganese (Mn), % 0 to 1.0
0 to 2.0
Nickel (Ni), % 0.6 to 1.1
9.0 to 13
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030