S41050 Stainless Steel vs. ASTM A229 Spring Steel

Both S41050 stainless steel and ASTM A229 spring steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is ASTM A229 spring steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
490 to 550
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
14
Fatigue Strength, MPa 160
710 to 790
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Shear Strength, MPa 300
1020 to 1140
Tensile Strength: Ultimate (UTS), MPa 470
1690 to 1890
Tensile Strength: Yield (Proof), MPa 230
1100 to 1230

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
50
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
19
Embodied Water, L/kg 97
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
200 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 140
3260 to 4080
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
60 to 67
Strength to Weight: Bending, points 17
40 to 43
Thermal Diffusivity, mm2/s 7.2
14
Thermal Shock Resistance, points 17
54 to 60

Alloy Composition

Carbon (C), % 0 to 0.040
0.55 to 0.85
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 84.2 to 88.9
97.5 to 99
Manganese (Mn), % 0 to 1.0
0.3 to 1.2
Nickel (Ni), % 0.6 to 1.1
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.050