S41050 Stainless Steel vs. EN 1.4724 Stainless Steel

Both S41050 stainless steel and EN 1.4724 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a very high 97% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is EN 1.4724 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
16
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
75
Shear Strength, MPa 300
340
Tensile Strength: Ultimate (UTS), MPa 470
550
Tensile Strength: Yield (Proof), MPa 230
280

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 720
850
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 27
21
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
2.0
Embodied Energy, MJ/kg 27
28
Embodied Water, L/kg 97
110

Common Calculations

PREN (Pitting Resistance) 12
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
73
Resilience: Unit (Modulus of Resilience), kJ/m3 140
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 7.2
5.6
Thermal Shock Resistance, points 17
19

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 0 to 0.040
0 to 0.12
Chromium (Cr), % 10.5 to 12.5
12 to 14
Iron (Fe), % 84.2 to 88.9
82.2 to 86.6
Manganese (Mn), % 0 to 1.0
0 to 1.0
Nickel (Ni), % 0.6 to 1.1
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0.7 to 1.4
Sulfur (S), % 0 to 0.030
0 to 0.015