S41050 Stainless Steel vs. EN 1.4971 Stainless Steel

Both S41050 stainless steel and EN 1.4971 stainless steel are iron alloys. They have 44% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is EN 1.4971 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
240
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 25
34
Fatigue Strength, MPa 160
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
81
Shear Strength, MPa 300
530
Tensile Strength: Ultimate (UTS), MPa 470
800
Tensile Strength: Yield (Proof), MPa 230
340

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
570
Maximum Temperature: Mechanical, °C 720
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 27
13
Thermal Expansion, µm/m-K 10
15

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
70
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.9
7.6
Embodied Energy, MJ/kg 27
110
Embodied Water, L/kg 97
300

Common Calculations

PREN (Pitting Resistance) 12
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
220
Resilience: Unit (Modulus of Resilience), kJ/m3 140
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 7.2
3.4
Thermal Shock Resistance, points 17
19

Alloy Composition

Carbon (C), % 0 to 0.040
0.080 to 0.16
Chromium (Cr), % 10.5 to 12.5
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Iron (Fe), % 84.2 to 88.9
24.3 to 37.1
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0.6 to 1.1
19 to 21
Niobium (Nb), % 0
0.75 to 1.3
Nitrogen (N), % 0 to 0.1
0.1 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0
2.0 to 3.0