S41050 Stainless Steel vs. EN 1.7106 Steel

Both S41050 stainless steel and EN 1.7106 steel are iron alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is EN 1.7106 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
200 to 500
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 470
660 to 2020

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Mechanical, °C 720
410
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
46
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.1
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
1.5
Embodied Energy, MJ/kg 27
20
Embodied Water, L/kg 97
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
24 to 73
Strength to Weight: Bending, points 17
22 to 46
Thermal Diffusivity, mm2/s 7.2
13
Thermal Shock Resistance, points 17
20 to 61

Alloy Composition

Carbon (C), % 0 to 0.040
0.52 to 0.6
Chromium (Cr), % 10.5 to 12.5
0.2 to 0.45
Iron (Fe), % 84.2 to 88.9
95.9 to 97
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Nickel (Ni), % 0.6 to 1.1
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
1.6 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.025