S41050 Stainless Steel vs. SAE-AISI 1035 Steel

Both S41050 stainless steel and SAE-AISI 1035 steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is SAE-AISI 1035 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
13 to 21
Fatigue Strength, MPa 160
210 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 300
360 to 370
Tensile Strength: Ultimate (UTS), MPa 470
570 to 620
Tensile Strength: Yield (Proof), MPa 230
300 to 530

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 720
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
18
Embodied Water, L/kg 97
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
79 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 140
250 to 740
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
20 to 22
Strength to Weight: Bending, points 17
19 to 21
Thermal Diffusivity, mm2/s 7.2
14
Thermal Shock Resistance, points 17
18 to 20

Alloy Composition

Carbon (C), % 0 to 0.040
0.32 to 0.38
Chromium (Cr), % 10.5 to 12.5
0
Iron (Fe), % 84.2 to 88.9
98.6 to 99.08
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Nickel (Ni), % 0.6 to 1.1
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050