S41050 Stainless Steel vs. SAE-AISI M1 Steel

Both S41050 stainless steel and SAE-AISI M1 steel are iron alloys. They have 87% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is SAE-AISI M1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 470
730 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1440
1560
Melting Onset (Solidus), °C 1400
1510
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 27
29
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
18
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.9
7.0
Embodied Energy, MJ/kg 27
99
Embodied Water, L/kg 97
98

Common Calculations

PREN (Pitting Resistance) 12
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
25 to 73
Strength to Weight: Bending, points 17
22 to 45
Thermal Diffusivity, mm2/s 7.2
8.0
Thermal Shock Resistance, points 17
23 to 66

Alloy Composition

Carbon (C), % 0 to 0.040
0.78 to 0.88
Chromium (Cr), % 10.5 to 12.5
3.5 to 4.0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 84.2 to 88.9
81 to 84.8
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 0
8.2 to 9.2
Nickel (Ni), % 0.6 to 1.1
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
1.4 to 2.1
Vanadium (V), % 0
1.0 to 1.4