S41050 Stainless Steel vs. C75700 Nickel Silver

S41050 stainless steel belongs to the iron alloys classification, while C75700 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is C75700 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 25
3.2 to 22
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 76
45
Shear Strength, MPa 300
350 to 370
Tensile Strength: Ultimate (UTS), MPa 470
590 to 610
Tensile Strength: Yield (Proof), MPa 230
470 to 580

Thermal Properties

Latent Heat of Fusion, J/g 270
200
Maximum Temperature: Mechanical, °C 720
180
Melting Completion (Liquidus), °C 1440
1040
Melting Onset (Solidus), °C 1400
990
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 27
40
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
30
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.9
3.6
Embodied Energy, MJ/kg 27
56
Embodied Water, L/kg 97
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
19 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
930 to 1410
Stiffness to Weight: Axial, points 14
7.8
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 17
19 to 20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 7.2
12
Thermal Shock Resistance, points 17
22 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.040
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
63.5 to 66.5
Iron (Fe), % 84.2 to 88.9
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.0
0 to 0.5
Nickel (Ni), % 0.6 to 1.1
11 to 13
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
19.2 to 25.5
Residuals, % 0
0 to 0.5