S42300 Stainless Steel vs. EN 1.7272 Steel

Both S42300 stainless steel and EN 1.7272 steel are iron alloys. They have 86% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is S42300 stainless steel and the bottom bar is EN 1.7272 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 1100
490 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
45
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 5.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.5
Embodied Energy, MJ/kg 44
19
Embodied Water, L/kg 110
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 39
17 to 59
Strength to Weight: Bending, points 30
18 to 40
Thermal Diffusivity, mm2/s 6.8
12
Thermal Shock Resistance, points 40
14 to 48

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.27 to 0.32
0.28 to 0.33
Chromium (Cr), % 11 to 12
0.4 to 0.55
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 82 to 85.1
97.2 to 98.3
Manganese (Mn), % 1.0 to 1.4
0.9 to 1.2
Molybdenum (Mo), % 2.5 to 3.0
0.1 to 0.15
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0.2 to 0.3
0