S44660 Stainless Steel vs. ACI-ASTM CB30 Steel

Both S44660 stainless steel and ACI-ASTM CB30 steel are iron alloys. They have 87% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S44660 stainless steel and the bottom bar is ACI-ASTM CB30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
210
Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
77
Tensile Strength: Ultimate (UTS), MPa 660
500
Tensile Strength: Yield (Proof), MPa 510
230

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 640
420
Maximum Temperature: Mechanical, °C 1100
940
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
21
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 21
10
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.3
Embodied Energy, MJ/kg 61
33
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 38
20
Resilience: Unit (Modulus of Resilience), kJ/m3 640
140
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 4.5
5.6
Thermal Shock Resistance, points 21
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.3
Chromium (Cr), % 25 to 28
18 to 21
Copper (Cu), % 0
0 to 1.2
Iron (Fe), % 60.4 to 71
72.9 to 82
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 1.0 to 3.5
0 to 2.0
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.040
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.040
Titanium (Ti), % 0.2 to 1.0
0