S44735 Stainless Steel vs. EN 1.4107 Stainless Steel

Both S44735 stainless steel and EN 1.4107 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S44735 stainless steel and the bottom bar is EN 1.4107 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 21
18 to 21
Fatigue Strength, MPa 300
260 to 350
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 82
76
Tensile Strength: Ultimate (UTS), MPa 630
620 to 700
Tensile Strength: Yield (Proof), MPa 460
400 to 570

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 650
390
Maximum Temperature: Mechanical, °C 1100
740
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 11
10

Otherwise Unclassified Properties

Base Metal Price, % relative 21
7.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 4.4
2.1
Embodied Energy, MJ/kg 61
30
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 42
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 520
420 to 840
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 23
22 to 25
Strength to Weight: Bending, points 21
21 to 22
Thermal Shock Resistance, points 20
22 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 28 to 30
11.5 to 12.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 60.7 to 68.4
83.8 to 87.2
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 3.6 to 4.2
0 to 0.5
Nickel (Ni), % 0 to 1.0
0.8 to 1.5
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.045
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0.2 to 1.0
0
Vanadium (V), % 0
0 to 0.080