S44735 Stainless Steel vs. EN 1.4317 Stainless Steel

Both S44735 stainless steel and EN 1.4317 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S44735 stainless steel and the bottom bar is EN 1.4317 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 21
17
Fatigue Strength, MPa 300
380
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 82
76
Tensile Strength: Ultimate (UTS), MPa 630
860
Tensile Strength: Yield (Proof), MPa 460
630

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 650
390
Maximum Temperature: Mechanical, °C 1100
770
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 11
11

Otherwise Unclassified Properties

Base Metal Price, % relative 21
10
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 4.4
2.4
Embodied Energy, MJ/kg 61
33
Embodied Water, L/kg 180
110

Common Calculations

PREN (Pitting Resistance) 42
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
130
Resilience: Unit (Modulus of Resilience), kJ/m3 520
1010
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 23
31
Strength to Weight: Bending, points 21
26
Thermal Shock Resistance, points 20
30

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 28 to 30
12 to 13.5
Iron (Fe), % 60.7 to 68.4
78.7 to 84.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 3.6 to 4.2
0 to 0.7
Nickel (Ni), % 0 to 1.0
3.5 to 5.0
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.045
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025
Titanium (Ti), % 0.2 to 1.0
0