S44735 Stainless Steel vs. CC767S Brass
S44735 stainless steel belongs to the iron alloys classification, while CC767S brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is S44735 stainless steel and the bottom bar is CC767S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 86 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 21 | |
| 34 |
| Poisson's Ratio | 0.27 | |
| 0.31 |
| Shear Modulus, GPa | 82 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 120 |
| Melting Completion (Liquidus), °C | 1460 | |
| 840 |
| Melting Onset (Solidus), °C | 1420 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 11 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 23 |
| Density, g/cm3 | 7.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 61 | |
| 47 |
| Embodied Water, L/kg | 180 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 520 | |
| 100 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 26 | |
| 20 |
| Strength to Weight: Axial, points | 23 | |
| 15 |
| Strength to Weight: Bending, points | 21 | |
| 16 |
| Thermal Shock Resistance, points | 20 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.1 to 0.8 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 28 to 30 | |
| 0 |
| Copper (Cu), % | 0 | |
| 58 to 64 |
| Iron (Fe), % | 60.7 to 68.4 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 3.6 to 4.2 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 to 1.0 |
| Niobium (Nb), % | 0.2 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.045 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0.2 to 1.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 32.8 to 41.9 |