S44735 Stainless Steel vs. SAE-AISI 1524 Steel

Both S44735 stainless steel and SAE-AISI 1524 steel are iron alloys. They have 65% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S44735 stainless steel and the bottom bar is SAE-AISI 1524 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 21
14 to 22
Fatigue Strength, MPa 300
230 to 340
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 82
73
Shear Strength, MPa 390
360 to 390
Tensile Strength: Ultimate (UTS), MPa 630
570 to 650
Tensile Strength: Yield (Proof), MPa 460
320 to 540

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 61
19
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
84 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 520
270 to 760
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 26
24
Strength to Weight: Axial, points 23
20 to 23
Strength to Weight: Bending, points 21
19 to 21
Thermal Shock Resistance, points 20
18 to 21

Alloy Composition

Carbon (C), % 0 to 0.030
0.19 to 0.25
Chromium (Cr), % 28 to 30
0
Iron (Fe), % 60.7 to 68.4
98 to 98.5
Manganese (Mn), % 0 to 1.0
1.4 to 1.7
Molybdenum (Mo), % 3.6 to 4.2
0
Nickel (Ni), % 0 to 1.0
0
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.045
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Titanium (Ti), % 0.2 to 1.0
0