S44735 Stainless Steel vs. Type 1 Magnetic Alloy

Both S44735 stainless steel and Type 1 magnetic alloy are iron alloys. They have 55% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S44735 stainless steel and the bottom bar is Type 1 magnetic alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 21
4.0 to 38
Poisson's Ratio 0.27
0.3
Shear Modulus, GPa 82
72
Tensile Strength: Ultimate (UTS), MPa 630
500 to 830
Tensile Strength: Yield (Proof), MPa 460
220 to 790

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 21
31
Density, g/cm3 7.7
8.3
Embodied Carbon, kg CO2/kg material 4.4
5.6
Embodied Energy, MJ/kg 61
77
Embodied Water, L/kg 180
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
33 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 520
130 to 1690
Stiffness to Weight: Axial, points 15
12
Stiffness to Weight: Bending, points 26
23
Strength to Weight: Axial, points 23
17 to 28
Strength to Weight: Bending, points 21
17 to 24
Thermal Shock Resistance, points 20
16 to 26

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 28 to 30
0 to 0.3
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 60.7 to 68.4
50.7 to 56.5
Manganese (Mn), % 0 to 1.0
0 to 0.8
Molybdenum (Mo), % 3.6 to 4.2
0 to 0.3
Nickel (Ni), % 0 to 1.0
43.5 to 46.5
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.045
0
Phosphorus (P), % 0 to 0.040
0 to 0.010
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0.2 to 1.0
0