S44800 Stainless Steel vs. EN AC-21200 Aluminum

S44800 stainless steel belongs to the iron alloys classification, while EN AC-21200 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S44800 stainless steel and the bottom bar is EN AC-21200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
120 to 130
Elastic (Young's, Tensile) Modulus, GPa 210
71
Elongation at Break, % 23
3.9 to 6.2
Fatigue Strength, MPa 300
110 to 130
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 82
27
Tensile Strength: Ultimate (UTS), MPa 590
410 to 440
Tensile Strength: Yield (Proof), MPa 450
270 to 360

Thermal Properties

Latent Heat of Fusion, J/g 300
390
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1460
660
Melting Onset (Solidus), °C 1410
550
Specific Heat Capacity, J/kg-K 480
880
Thermal Conductivity, W/m-K 17
130
Thermal Expansion, µm/m-K 11
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
34
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
100

Otherwise Unclassified Properties

Base Metal Price, % relative 19
10
Density, g/cm3 7.8
3.0
Embodied Carbon, kg CO2/kg material 3.8
8.0
Embodied Energy, MJ/kg 52
150
Embodied Water, L/kg 190
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
16 to 22
Resilience: Unit (Modulus of Resilience), kJ/m3 480
500 to 930
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
46
Strength to Weight: Axial, points 21
38 to 40
Strength to Weight: Bending, points 20
41 to 43
Thermal Diffusivity, mm2/s 4.6
49
Thermal Shock Resistance, points 19
18 to 19

Alloy Composition

Aluminum (Al), % 0
93.3 to 95.7
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.15
4.0 to 5.0
Iron (Fe), % 62.6 to 66.5
0 to 0.2
Lead (Pb), % 0
0 to 0.030
Magnesium (Mg), % 0
0.15 to 0.5
Manganese (Mn), % 0 to 0.3
0.2 to 0.5
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 2.0 to 2.5
0 to 0.050
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.2
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
0 to 0.030
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.1